  CK45 Cylinder piston rod is a very important part in hydraulic cylinder working smoothly,hard chrome plating a piece of precision equipment such as a cylinder rod is a painstaking and methodical process. As one of the leading CK45 chrome plated bar suppliers and manufacturers, DTONG   GROUP   has been supplying and exporting CK45 hard chrome bar and hard chrome rod for almost 20 years with high quality & good prices.Imperial sizes & metric sizes available. The Hard Chrome Plating Process: 1. Inspection The  CK45 cylinder chrome rod  is inspected during the initial evaluation to determine the condition prior to the chroming process. An inspector will make note of any signs of corrosion, pitting, marring, damage, cracking or flaking. The presence of any of these conditions will be taken into account during the re-chroming process. 2. Grinding & Stripping Old material on the  hydraulic cylinder rod  must be removed before new chrome can be a...

  S45C Hard Chrome Plated Steel Bar usually used for producing hydraulic cylinder piston rods,It goes through the machining process of cold drawn , peeling,  grinding, polishing, and hard chrome plating , in order to enhance the surface hardness for friction and corrosion resistance; the material will also be easier for further machining, and its precision can achieve international standard.The S45C  chrome plated rods can be application for Join Pen, High-Strength Screw, Bolting, Sliding Bar and Auto Parts.For Plastic Machines parts: Main Rods, Screw Bars and Feeding Bars.Features: Material：JIS S45C、SAE1045、DIN CK45、EN8 Application：Pneumatic/ Hydraulic Cylinder , Engineering Machine, Hydraulic/ Pneumatic Auto Machine, Plastic Injection Molding Machine. Thickness of Chrome Layer：min 20/25/30/50 Micron or customized Hardness of Chrome Layer： HV850 min. (0.1) Surface Roughness：Ra 0.2μm max. External Diameter Accuracy：ISO h7、f7、h8、f8、g6 Straightness： 0.5/1000 Roundness： Ra...

 SAE 4140 steel can be used in a ready-made semi-hardened ( quenched + tempered ) state. Its hardness is in the range of 28-32 HRc. It is a material known as tempering steel in the industry, which can be used in hydraulic cylinder shafts , gears, and machine parts working under high tensile strength thanks to its high tensile strength. 4140 is a medium-carbon (nominal 0.40%C) chromium-molybdenum alloy steel that is most often oil quenched to attain an as-quenched hardness ranging from about 54-59 HRC (as quenched), depending on the precise carbon content (which affects the hardenability of the material). Applications of Grade 4140 Quench +Tempered Medium-high stressed 4140  shafts and components where the use of carbon steel 1045 would not be appropriate. Reasons for using 4140 are the higher yield and fatigue strength, better through hardening of the material and superior impact properties compared to plain carbon steels like 1045. These advantages are only achieved when 414...