THE APPLICATION OF DIN 2391 ST35 NBK SEAMLESS TUBES

 DIN 2391 ST35 NBK Seamless Tubes come under AISI, DIN, EN, GB and other international standard specifications. they range from 4mm to 219mm in outer diameter with wall thicknesses ranging from 0.5mm to 20mm.  ST35 Seamless tubes are frequently used for high heat and pressure applications in oil and gas(high pressure oil pipes) petrochemical, hydraulic cylinders & pneumatic cylinder,mechanical and Automotive engineering petroleum, and other industries. They come in various sizes and forms, including round, square, and U-shaped. Furthermore, these stainless steel tubes’ strength and corrosion resistance are well known. They are frequently produced with a seamless finish and can be used in many different sectors. ST35 is one of the best choices among the various types of steel tubes for low-cost, low-corrosion pipes. It has muscular tensile and yield strength and may be formed into round, square, or oval tubes. These stainless steel tubes’ ability to be welded without any pre-heating is their principal benefit. It makes them very simple to use and facilitates more straightforward manufacturing procedures.

Chemical Composition

StandardGradeChemical Components (%)
SymbolMaterial No.CSiMnPS
DIN2391St 351.0308≤0.17≤0.35≥0.40≤0.025≤0.025

Delivery Conditions

The ST35 seamless tubes shall be manufactured from cold drawn or cold rolled processes. The tubes shall be supplied in one of the delivery conditions as follows:

DesignationSymbolDescription
Cold finished (hard)BKTubes do not undergo heat treatment following the final cold forming and thus, have a rather high resistance to deformation.
Cold finished (soft)BKWThe final heat treatment is followed by cold drawing involving limited deformation. Appropriate further processing allows a certain degree of cold forming (e.g. bending, expanding).
Cold finished and stress-relievedBKSHeat treatment is applied following the last cold forming process. Subject to appropriate processing conditions, the increase in the residual stresses involved enables both forming and machining to a certain degree.
AnnealedGBKThe last cold forming process is followed by annealing in a controlled atmosphere.
NormalizedNBKThe last cold forming process is followed by annealing above the upper transformation point in a controlled atmosphere.

Comments

Post a Comment

Popular posts from this blog

How to deal with the scratch on the surface of hydraulic cylinder barrel

Image
As we all know,In the process of using the  hydraulic cylinder , the hydraulic cylinder barrel will be damaged,it is common that there will be scratch on the surface of the  honed tube , some customers will ignore these scratches, this to us is not responsible for the cylinder, when a small scratches in the cylinder,we usually take some tips to deal with them. 1.First,  to clean up the oil on the surface of our hydraulic cylinder barrel, then we will use the grinder machine to the surface treatment of the scratched part of our cylinder, at this time we have to grind the surface of the cylinder wall out of swallowtail groove. Although we have cleaned our cylinder at the beginning, at this time we need to clean the cylinder barrel further. At this time, we use anhydrous ethanol to clean the surface of the scratch repair of honed cylinder barrel. 2. We usually use special  repairing adhesive  to solve the scratches on the surface of  hydraulic cylinder barrel ...
Read more

Heat Treatments Of Seamless Steel Tube

Image
Heat treatment of  seamless steel tubes  is a process to improve the properties of metal materials and their products. Depending on the use, the material and its workpiece are heated to the appropriate temperature, insulated, and then cooled in different ways to alter the internal structure to achieve the desired performance. Heat treatment of seamless steel tubes is generally divided into annealing, normalizing, quenching, tempering, failure, chemical heat treatment and vacuum heat treatment. By heat treatment, the efficiency or life of the steel can be improved, and in some cases, more expensive special materials can be used instead of cheaper ordinary metal materials. The basic heat treatment methods of seamless steel tubes mainly include the following four forms: 1. Annealing Annealing is a process in which a seamless steel tube is heated to a slightly higher or lower critical temperature for a period of time (ie, heat preservation) and then slowly cooled. Common annealing...
Read more

HOW TO REPAIR THE HYDRAULIC CYLINDER ROD

  Hydraulic cylinders can be repaired, but you should never attempt these repairs on your own. Although hydraulic cylinders have a simple design, you must be familiar with them in order to efficiently repair them. When a technician performs hydraulic cylinder repairs, they take the entire mechanism apart and reassemble to find the root cause of the issue. COMMON POINTS OF HYDRAULIC CYLINDER FAILURE There are several common points of hydraulic cylinder failure. These include the piston, cylinder rod , seals, and head. PISTON The pistons in hydraulic cylinders are one of the most common points of failure. This is especially true in light-duty applications. The pistons used in light-duty applications are often made from aluminum, which wears out much more quickly than the steel used in heavy-duty applications. When checking pistons for failure, technicians will often measure the diameter of the piston. The piston’s diameter in relation to the bore directly affects the amount of hydra...
Read more