THE MECHANICAL PROPERTIES OF SCM430 ROUND BAR

 SCM430 is a chromium-molybdenum alloy steel as per Japan Standard. JIS SCM430 steel contains a lower carbon content but provides better weldability comparing with SCM440 Steel. SCM430 round bar is frequently applied to the gas & oil area.Typical applications include components such as valve  bodies,pumps and hydraulic cylinder fittings like cylinder rod.

Chemical Composition
National
Standard		GradeC%Si%Mn%Cr%Mo%P%S%
DIN25CrMo4
(1.7218)		0.22-0.29≤0.40.6-0.90.9-1.20.15-0.3≤0.025≤0.035
AISI/SAE41300.28-0.330.15-0.350.4-0.60.8-1.10.15-0.25≤0.035≤0.04
JISSCM4300.28-0.330.15-0.350.6-0.850.9-1.20.15-0.3≤0.035≤0.04
GB30CrMo 0.26-0.34 0.17-0.37 0.4-0.7 0.8-1.1 0.15-0.25 ≤0.035 ≤0.035

SCM430 ROUND BAR FORGING

Forging temperature of AISI 4130 steel should be carried out between 950℃-1200℃,The lower the forging-ending temperature ,the finer the grain size .Hold suitable time for the steel to be uinformly heated before forge, but don’t forge below 950℃.AISI 4130 steel should be cooled as slowly as possible after forged.

SCM430 ROUND BAR HEAT TREATMENT

4130 Annealing

AISI 4130 steel can be annealed to relieve stress after forging ,and obtain a good structure suitable for machining,Annealing temperature should be carried out between 800℃-850℃, hold suitable time for the steel to be heated uniformly. Cool slowly in the furnace.

4130 Normalizing

Normalizing is used to refine the structure of forgings that might have cooled non-uniformly after forged,and considered as a conditioning treatment before final heat treatment.Normalizing temperature for AISI 4130 steel should be carried out between 880℃-900℃. hold suitable time for the steel to be uniformly heated to complete the ferrite to austenite transformation.Cool in still air.

4130 Tempering

Tempering is usually carried out to relieve stresses from the hardening process, and will optimize hardness and mechanical properties. The actual tempering temperature will be chosen to meet the required properties.Heat the AISI 4130 carefully to a suitable temperature ,usually between 400℃-570℃, soak at the temperature for 2 hours per 25mm of ruling section, then cool in air.The lower the tempering temperature the greater the strength. However, Tempering between 250-375°C is not advised as tempering within this range will seriously reduce the impact value.

Hardening of SCM430 Round Bar

This heat treatment will obtain martensite structure after quenched,it will increase the surface hardness and strength.AISI 4130 steel should be carried out between 870℃-890℃, hold suitable time for the steel to be thoroughly heated, then quench in oil, or water.Tempering should be followed immediately after quenched.

Datong Hydraulic as a professional steel tubes and rods manufacturer,we have rich experience in the production and export for SCM430 round bar , we also supply 4140 4130 4340 hard chrome cylinder rod ,hollow chrome bar, induction hardened rod for all size. Contact us now for more informations.

Comments

Post a Comment

Popular posts from this blog

How to deal with the scratch on the surface of hydraulic cylinder barrel

Image
As we all know,In the process of using the  hydraulic cylinder , the hydraulic cylinder barrel will be damaged,it is common that there will be scratch on the surface of the  honed tube , some customers will ignore these scratches, this to us is not responsible for the cylinder, when a small scratches in the cylinder,we usually take some tips to deal with them. 1.First,  to clean up the oil on the surface of our hydraulic cylinder barrel, then we will use the grinder machine to the surface treatment of the scratched part of our cylinder, at this time we have to grind the surface of the cylinder wall out of swallowtail groove. Although we have cleaned our cylinder at the beginning, at this time we need to clean the cylinder barrel further. At this time, we use anhydrous ethanol to clean the surface of the scratch repair of honed cylinder barrel. 2. We usually use special  repairing adhesive  to solve the scratches on the surface of  hydraulic cylinder barrel ...
Read more

Heat Treatments Of Seamless Steel Tube

Image
Heat treatment of  seamless steel tubes  is a process to improve the properties of metal materials and their products. Depending on the use, the material and its workpiece are heated to the appropriate temperature, insulated, and then cooled in different ways to alter the internal structure to achieve the desired performance. Heat treatment of seamless steel tubes is generally divided into annealing, normalizing, quenching, tempering, failure, chemical heat treatment and vacuum heat treatment. By heat treatment, the efficiency or life of the steel can be improved, and in some cases, more expensive special materials can be used instead of cheaper ordinary metal materials. The basic heat treatment methods of seamless steel tubes mainly include the following four forms: 1. Annealing Annealing is a process in which a seamless steel tube is heated to a slightly higher or lower critical temperature for a period of time (ie, heat preservation) and then slowly cooled. Common annealing...
Read more

HOW TO REPAIR THE HYDRAULIC CYLINDER ROD

  Hydraulic cylinders can be repaired, but you should never attempt these repairs on your own. Although hydraulic cylinders have a simple design, you must be familiar with them in order to efficiently repair them. When a technician performs hydraulic cylinder repairs, they take the entire mechanism apart and reassemble to find the root cause of the issue. COMMON POINTS OF HYDRAULIC CYLINDER FAILURE There are several common points of hydraulic cylinder failure. These include the piston, cylinder rod , seals, and head. PISTON The pistons in hydraulic cylinders are one of the most common points of failure. This is especially true in light-duty applications. The pistons used in light-duty applications are often made from aluminum, which wears out much more quickly than the steel used in heavy-duty applications. When checking pistons for failure, technicians will often measure the diameter of the piston. The piston’s diameter in relation to the bore directly affects the amount of hydra...
Read more