THE HARDNESS OF CK45 INDUCTION HARDENED CHROME PLATED BAR

Ck45 induction hardened chrome plated bar is used extensively by the hydraulic and pneumatic industries, for those applications utilising its high surface hardness and excellent resistance to surface impact.

Induction hardened: Induction hardened is a form of heat treatment in which a metal part is heated by induction heating. Induction hardening of piston rods in hydraulic cylinders is performed in order to increase the resistance to damage from external impact in applications where there is risk for them. The hardness after this heat treatment is HRC 40 to 45.

Surface hardness: min. 900 HV0.1 (66 HRC) the surface hardness in the induction-hardened zone immediately beneath the chrome layer is min. 55 HRC (HV 595).

Hardening depth: 0.75 – 4.0mm depending on the diameter. Other hardening depths can be supplied by special arrangement.
Corrosion resistance: min. 120 – 200 hours in Neutral Salt Spray testing according to ISO 9227 standard or its equivalents, combined with evaluation according to ISO 10289. Rating ≥ 9. 500 and 1000 hours of corrosion resistance available on request.
Fields of application: this product is characterized by an extremely smooth surface finish with excellent wear and corrosion resistance, supported by an induction hardened case offering greater strength and resistance to mechanical damage, coupled with good core strength. It is recommended in applications requiring greater surface impact resistance.
induction hardened chrome plated bar

We are the leading manufacturer and supplier of CK45 induction hardened chrome plated bar that are manufactured using high quality raw material and advanced technology. Our offered CK45 round steel bar  product range includes Mild Steel Round Bars, Alloy Steel Round Bars, Bearing Steel Round Bars, Free Cutting Steel Round Bars and Carbon Steel Round Bars. These products are tested on various parameters in order to ensure flawlessness of the product. we also supply 4140 chrome plated rod, 1045 chrome rod, honed steel tube and hollow chrome bar. Welcome Your Inquirys.

Comments

Post a Comment

Popular posts from this blog

How to deal with the scratch on the surface of hydraulic cylinder barrel

Image
As we all know,In the process of using the  hydraulic cylinder , the hydraulic cylinder barrel will be damaged,it is common that there will be scratch on the surface of the  honed tube , some customers will ignore these scratches, this to us is not responsible for the cylinder, when a small scratches in the cylinder,we usually take some tips to deal with them. 1.First,  to clean up the oil on the surface of our hydraulic cylinder barrel, then we will use the grinder machine to the surface treatment of the scratched part of our cylinder, at this time we have to grind the surface of the cylinder wall out of swallowtail groove. Although we have cleaned our cylinder at the beginning, at this time we need to clean the cylinder barrel further. At this time, we use anhydrous ethanol to clean the surface of the scratch repair of honed cylinder barrel. 2. We usually use special  repairing adhesive  to solve the scratches on the surface of  hydraulic cylinder barrel ...
Read more

Heat Treatments Of Seamless Steel Tube

Image
Heat treatment of  seamless steel tubes  is a process to improve the properties of metal materials and their products. Depending on the use, the material and its workpiece are heated to the appropriate temperature, insulated, and then cooled in different ways to alter the internal structure to achieve the desired performance. Heat treatment of seamless steel tubes is generally divided into annealing, normalizing, quenching, tempering, failure, chemical heat treatment and vacuum heat treatment. By heat treatment, the efficiency or life of the steel can be improved, and in some cases, more expensive special materials can be used instead of cheaper ordinary metal materials. The basic heat treatment methods of seamless steel tubes mainly include the following four forms: 1. Annealing Annealing is a process in which a seamless steel tube is heated to a slightly higher or lower critical temperature for a period of time (ie, heat preservation) and then slowly cooled. Common annealing...
Read more

HOW TO REPAIR THE HYDRAULIC CYLINDER ROD

  Hydraulic cylinders can be repaired, but you should never attempt these repairs on your own. Although hydraulic cylinders have a simple design, you must be familiar with them in order to efficiently repair them. When a technician performs hydraulic cylinder repairs, they take the entire mechanism apart and reassemble to find the root cause of the issue. COMMON POINTS OF HYDRAULIC CYLINDER FAILURE There are several common points of hydraulic cylinder failure. These include the piston, cylinder rod , seals, and head. PISTON The pistons in hydraulic cylinders are one of the most common points of failure. This is especially true in light-duty applications. The pistons used in light-duty applications are often made from aluminum, which wears out much more quickly than the steel used in heavy-duty applications. When checking pistons for failure, technicians will often measure the diameter of the piston. The piston’s diameter in relation to the bore directly affects the amount of hydra...
Read more